Saygili, Y. S., Cakmak, B. (2023). Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods. , 25(1), 47-59. doi: 10.52547/jast.25.1.47
Y. S. Saygili; B. Cakmak. "Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods". , 25, 1, 2023, 47-59. doi: 10.52547/jast.25.1.47
Saygili, Y. S., Cakmak, B. (2023). 'Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods', , 25(1), pp. 47-59. doi: 10.52547/jast.25.1.47
Saygili, Y. S., Cakmak, B. Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods. , 2023; 25(1): 47-59. doi: 10.52547/jast.25.1.47

Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods

Journal of Agricultural Science and Technology
Article 4, Volume 25, Issue 1, 2023, Pages 47-59    PDF (9.8 M)
Document Type: Original Research
DOI: 10.52547/jast.25.1.47
Authors
Y. S. Saygili* 1; B. Cakmak2
1Department of Biosystem Engineering, Faculty of Agricultural Sciences and Technologies, Niğde Ömer Halisdemir University, Niğde, Turkey.
2Department of Agricultural Machinery and Technologies Engineering, Faculty of Agriculture, Ege University, İzmir, Turkey.
Abstract
Surfaces of the toothed harrow were improved by using different coating materials and methods. Four different coating methods and special alloy powders were used as coating materials. TiCN was applied with PVD, and the WC-Ni-Co-Cr-Si-Fe-B powder mixture was applied with HVOF. The coating thicknesses was 2 µm and 5 µm in PVD, 500 µm in the HVOF, and 500+2 µm in the application where HVOF + PVD were used together. The wear trials were carried out in the laboratory, at a 50 km distance, in a double-speed trial pattern that converted circular motion to linear motion. The trial model was used to simulate the wear that occurs under real operating conditions in the soil. As a result of the wear trials carried out under the same operating conditions, a total material loss of 3.99 g occurred in the control (uncoated) harrow, the wear resistance increased, and less material loss was observed in the coated harrows. The sample coated with the PVD method had the lowest value with a material loss of 0.14 g. Material loss for other coated samples PVD-5µ, HVOF-500µ, and PVD-2µ+HVOF-500µ was 0.19, 0.28, and 0.18 g, respectively. When the amount of wear in the uncoated sample was 100%, the proportional loss in PVD-2µ, PVD-5µ, HVOF-500µ, and PVD-2µ+HVOF-500µ coated samples was calculated as 3.41, 4.85, 7.16, and 4.57%, respectively.
Keywords
Agricultural machinery; Abrasion; Material loss; Coating
References
Statistics
Article View: 171
PDF Download: 118
Statistics
Number of Journals45
Number of Issues2,171
Number of Articles24,674
Article View24,452,386
PDF Download17,557,095